Belarus using technology to build a better PM industry
special feature
Belarus using technology to build a better PM industry The countries of the former Eastern Bloc are using PM technologies developed during the Soviet era but combining and sharpening them by the use of imported new technologies…
I
n a country which is around 40 per cent forested and in which agriculture and forestry are major industries, it comes as no particular surprise that much of the powder metallurgy industry of Belarus is devoted to the manufacture of parts for heavy machinery, agricultural and otherwise, that can either be deployed within the country or sold as exports. Professor Alex Ilyushenko of the Powder Metallurgy Institute in the National Academy of Sciences says that there are 16 specialised companies and associations engaged in powder metallurgy in modern Belarus. “The main research and the greatest volume of production output are concentrated under the auspices of the Minsk-Molodecheno Powder Metallurgy Association. Some 2055 tons of construction, tribo-technical and electrotechnical products were made and delivered in Belarus in 2007.” The industry is modernising. Technology for hot pressing of plasticised powder mixtures was adopted in 2007-2008 and modern technology for high-temperature sintering and hardening of parts from powder steels is in use. Sintering is developing a high-tech aspect in Belarus with the introduction of selective laser sintering of metal powders.
24
MPR April 2009
In manufacturing, pilot and industrial batches of PM “block rings” for the Belarus tractor gearbox have been delivered. Production technology has been optimised to minimise post-manufacture finishing and the first batch of integrated cone ring parts has been delivered. An industrial batch of parts for hand tools has also been delivered. Physical vapour deposition methodology in the copper-plating industry is planned for introduction in the near
100
future, replacing galvanic methods currently in use. Spreading the arc of powder technology, Belarus is developing ceramic injection moulding and has already seen some success. Pilot samples of parts of alumina-based pneumodrive distributor system for lorry brakes have been delivered and zirconia-based watch bodies have been made by ceramic injection moulding. The main PM trends in Belarus are:
100
300
755
100 179
200
Molodechno PM Plant
BATE
PM Institute
BelAZ
Ferrit Ent.
Ertex Ent.
All Figure 1. Powder production output in the Republic of Belarus from different plants in 2007.
0026-0657/09 ©2009 Elsevier Ltd. All rights reserved.
å 3DUWV IRU PRWRU DQG WUDFWRU DQG DJULculture machines- frictional disks and friction assembly linings; sliding bearings, gears and synchronisers; å (OHFWURWHFKQLFDO SDUWV IRU HOHFWULF machine collectors, electric brushes, electric contacts, hard and soft magnetic ferrites and ceramic isolators; å 3URGXFWLRQRISRURXVSURGXFWVIRUILOtration of liquids, gases, metal melts, heat exchangers, noise silencers and fire barriers; å 3URGXFWLRQ RI SRZGHUV IRU KDUG DQG soft magnetic soft ferrites, bronze and special powders for gas and thermal spraying; å *DVDQGWKHUPDODQGLRQDQGYDFXXP methods for applying wear and corrosion-resistant coatings as well as decorative coatings; å 'LDPRQGWRROSURGXFWLRQ The products of the 16 PM enterprises mentioned above powder metallurgy are varied, and used for both in-house assembly shop completion in bigger enterprises and for delivery to other consumers (Figure 1). Products of black and coloured metals powders, frictional compositions on steel bases and ferrite powder products are used more widely in the country. More than 700 tons of construction and anti-frictional products; about 1000 tons of ferrite powder products; more than 200 tons of electro-technical products( such as collectors for starters and electric brushes) and more than four tons of hard alloy products were manufactured in 2007. (Figure 2) Professor Ilyuschenko: “A number of technological processes protected by patents of Republic of Belarus and other countries have been developed and adopted under industrial conditions by Powder Metallurgy Institute specialists together with Production Republican Unitary Republican Production Enterprise of the Molodecheno Powder Metallurgy Plant to make parts from metal powders. Cold stamping of sintered parts made from black and coloured metal powders, the peculiarity of which are great plastic changes in sintered material form accompanied by its intensive packing and strengthening. “Car starter motor parts that are the equal of products manufactured by traditional metal working are made using to this technology. The method devel-
metal-powder.net
6 306
3 400
290 629
Ferrits
Structural parts and slide bearing
Frictional disks and klutchs
Electrotechnikal parts
Hard metal
Porous materials and heat pipe
Figure 2. Issue output for different types of powder production in the Republic of Belarus..
oped for sintering multi-component frictional material on steel bases is characterised by higher efficiency than traditional methods. The process is widely used in Production Republican Unitary Republican Production Enterprise’s PM plant in Molodecheno and State Powder Metallurgy Research Institute in making frictional disks.” The technology for solder – sintering of freely sprinkled frictional layers on steel base without galvanic copper coating introduced what is essentially a simplified technology for making frictional disks (Figure 3). As in the case of traditional soldering process, the connected surfaces are processed with a liquid solution of active flux to remove oxides from the base layer surface as well as for protection of connected surfaces from interaction with the environment, for reduced surface tension and increased spreading of liquid soldering agents. The composition developed -
“active water flux” – is a mixture of zinc chloride, ammonia chloride and copper chloride salts. Its interaction with iron leads to the formation of easily melted iron chloride. An active reducer for surface oxides is the nitrogen and hydrogen sintering furnace atmosphere. The solder – sintering process is carried out by passing the discs through belt furnaces. Subsequent operations are identical to the traditional technology The strength of items such as frictional disks for tractors, made by Belarusdeveloped technology, are certified by bending tests, as shown in Figure 3. As seen, the strength of the bimetal compound is high, a 180° bend does not result in separation of soldered metal ceramics and the steel base stripping. That is the main requirement for operational quality control of compound strength. Pilot data have shown that the strength of soldered compound-steel *IULFWLRQDOPDWHULDO0.FRQVWLWXWHV
Figure 3. Tractor frictional disk with two-sided soldered frictional layer after tests on compound strength.
April 2009 MPR
25
Figure 4. Experimental samples of cone ring parts for the synchroniser assemblies of tractor gearboxes.
5.41-5.6MPa which is by 10% better than the compound strength obtained by traditional method of applying freely sprinkled layer on coppered base. The replacement of the intermediate galvanic copper sub-layer by PM copper increased intermediate strength by 10-15%. This combination has proved to be cheaper and ecologically better since the galvanic copper plating process has come to an end. In a further development hard flux has been introduced into the frictional material, providing a further ecological boost and cost reduction. The method for producing heavily loaded sliding bearings with the use of infiltration of steel sintered bodies by
antifriction bronze melts is very promising. Such bearings are used in pivots of the front suspension bracket of dump trucks and lorries. Similar technology is also used in making bimetal bodies of blocks of axial and piston pumps and motors in which working surfaces are coated with anti-frictional powder layers. To carry out calculations and completion of technological processes for obtaining PM construction by hot pressing, the properties of diffused and alloyed powders of the following compoVLWLRQV 'LVWDOR\ $( & XVHG IRU making block rings of synchronisers for à%HODUXVá JHDUER[HV DQG 'LVWDOR\ '&
Figure 5. Experimental sample parts of a car braking system made by ceramic injection moulding of alumina-based ceramics.
26
MPR April 2009
0,3%C for making cone rings for synchroQLVHUVZHUHUHVWXGLHG'HQVPL[SRZGHU RQWKHEDVLVRI'LVWDOR\$(JUDSKLWHDQGSODVWLFLVHU'1KDVWKH following chemical composition: iron – base; molybdenum – 0.5%; nickel – 4%, copper – 15%, graphite –0.3% [5]. On the basis of literature data analysis and experimental investigation performance, the following main properties of materials under study were defined: fluidity of powders, sprinkled density, density- temperature and pressing pressure relationship curve, elastic after action, Poisson coefficient, Young’s modulus and fluidity limit. Taking into consideration the data obtained, we cal-
Figure 5a. Experimental samples of watch bodies obtained by CIM from zirconium ceramics.
metal-powder.net
a
b
c
Figure 6. Selective laser sintering installation developed in the Powder Metallurgy Institute.: a – general view; b –working chamber; c –technology platform
culated the optimal cycle for heat pressing stepped parts such as a ring with clamp and experiments on technology completion for obtaining block rings for a synchroniser of a “Belarus” tractor gearbox were carried out. Total density of block ring pressing pressed from 'LVWDOR\ $( SRZGHU E\ KHDW SUHVVLQJ method was 7.2 – 7.25g/ cm3. Shrinkage after sintering was 0.5%. It has been established that the blocking ring tooth after sintering has the greatest density in comparison with other elements. At
metal-powder.net
the same time, tooth density at the top, at 7.31g/cm3, is lower than the density at the base, 7.37g/cm3. The ring hub also has irregular density distribution. The influence of heat pressing, temperature and sintering time on material structure, properties and sizes of FRQH ULQJV PDGH IURP SRZGHU 'LVWDOR\ AE with additive 0.6%C has been studied. (Figure 4) If the synchroniser block rings are produced by thermal pressing methods by a number of companies, the attempt to get a constantly loaded cone
ring by this technology and in accordance with our data is a first. It has been established that sizes of pressing obtained by heat pressing increase by 0.1 – 0.2%. After sintering at 1170˚C in a nitrogen and hydrogen atmosphere they 0.4% – 0.5%. Parts sintered at 11700C for an hour have higher mechanical properties and satisfactory hardness (170 HB) for subsequent final plastic deformation. Annealing at 750 ˚C for two hours and slow cooling leads to reduced hardness of ring up to 140-160
April 2009 MPR
27
140-160 HB. Calibration for obtaining required sizes must be made after pressure annealing to 650 MPa. The problem for obtaining products of complex form, exact sizes and high density can be solved with the use of modern technology and equipment for injection forming of powder materials. The Powder Metallurgy Institute has acquired an installation for metal and ceramic injection moulding (MIM/CIM) for investigating processes of injection forming of complex form products of plasticised mixtures of metal or ceramic powders with part volumes up to 100 cm3, and maximum casting pressure up to 100 MPA. Additionally researchers are looking at other parameters such as granule bin heating up to temperatures of 150 – 200˚C; cast form locking effort of 250 – 310 MPA; productivity up to 20 cycles per hour (not less than 3 kg per hour). The first samples of parts – golden couple of pneumodrive system of car brakes (Figure 5) and watch body (Figure 5a) were obtained from plasticized ceramic mixtures Catamould. Multipurpose installation of powder laser stereolithography (selective laser sintering) has been developed and made by Powder Metallurgy Institute. It has a set of unique technology possibilities and great investigative potential [7] (Figure 6). The installation is designed for obtaining solid products of complex form made from metal and polymer powders. The system produces high precision components and the Institute has not spared expenditure on preparation or marketing of finished products. The equipment installed can operate as a laser sintering device or be used for laser melting. In the first case, surface melting of powder particles in layers and their combination by forming liquid metal contact necks is what allows in most cases porous the creation of products with given operational properties in preserving structure and phase composition of the initial material. In the second case, full powder melting in layer is used and products are obtained with virtually zero porosity. The installation is designed for sintering a wide range of materials, the melting temperature of which can differ. The total dimensions of soldering products do not exceed 50 ⫻ 200 ⫻ 200. Powders,
28
MPR April 2009
preferably spherical, with the size from 20µ to 400µ are used for sintering. Laser radiation is focused and directed perpendicular to the sintered layer plane. The selective laser sintering process occurs on vertically moving technology platform with the help of a linear step drive. The platform is located in working chamber with a protective atmosphere. The delivery of powder portions to the technology platform and formation of powder layers with given thickness is carried out with the help of a scale. Laser ray scanning in the horizontal plane at a given trajectory and sintering area observation with the help of video is made with the help of an optical system installed on two mutually perpendicularly connected linear step drives. Laser radiation is generated by an optic quant generator on the basis of a monocrystalline alumo-yttrium garnet alloyed by trivalent neodymium <$* 1G), working at a wavelength of 1064 nm (infrared radiation) with impulse repetition frequency up to 50 Hz. The preparation of the virtual model of product, software control for installation work, technology mode designation and their control in a real time regime is carried through by overall computer control. Professor Ilyuschenko says: “Powder metallurgy in Belarus is developing successfully. Advanced imported technologies are being adopted and are supporting and enhancing core knowledge already in the country. The opportunities provided by new technologies are being taken by researchers in the republic’s research institutes and the larger enterprises.The priority trend is the development of new sintered frictional materials, improved technology of production of frictional disks for tractor and road making vehicles. Our own investigations are carried out and new technologies for formation of powders according to selective laser sintering method are being developed.”
References 1. 40 years of powder metallurgy in the Republic of Belarus/ under editorVKLS RI ($ 'RURVKNHYLFK 9LW\D] 3 A, Zharin A E, Ilyushchenko A Ph et DO 0LQVN à.RYFKHJá S LQ Russian). 2. Modern sintered friction materiDOV 'PLWURYLFK $ $ ,O\XVKFKHQNR $
3.
4.
5.
6.
7.
3K 6\URH]KNR * 6 6KLSLWVD 1 $ Materials of reports of International Specialised scientific and engineering workshop,Minsk, April 15-16 2008. Minsk: Powder Metallurgy Institute, 2008, p.6-14 (in Russian) Frictional layer soldering to steel EDVH6\URH]KNR*63DVKFKXN6( *UL]HO39HWDO3RZGHUPHWDOOXUJ\ on motor and tractor machine building. Welding and cutting of materials .Materials, technologies and equipment for applying protective coating: International scientific and engineering symposiums, Minsk, March 28-30, 2007: materials of reports.Minsk: Powder Metallurgy Institute, 2007,p.34-38 ( in Russian). Tribotechnical properties of powder antifrictional materials used for friction assembly of axial and piston pumps/ '\DFKNRYD / 1 9RURQHWVND\D /
The authors This feature draws on Powder metallurgy of Belarus: science and production, a SDSHUE\$,O\XVFKHQNR96DYLFKDQG * 6\URHJNR ZKR DUH OHDGLQJ UHVHDUFKers in the Belarus industry. It was given at Euro PM 2008 in Mannhiem. 1. Powder Metallurgy Institute of NASc of Belarus, 41, Platonov Str., Minsk, 220005 Belarus 2. Molodechno Powder Metallurgy Plant,
metal-powder.net
Belarus using technology to build a better PM industry The countries of the former Eastern Bloc are using PM technologies developed during the Soviet era but combining and sharpening them by the use of imported new technologies…
I
n a country which is around 40 per cent forested and in which agriculture and forestry are major industries, it comes as no particular surprise that much of the powder metallurgy industry of Belarus is devoted to the manufacture of parts for heavy machinery, agricultural and otherwise, that can either be deployed within the country or sold as exports. Professor Alex Ilyushenko of the Powder Metallurgy Institute in the National Academy of Sciences says that there are 16 specialised companies and associations engaged in powder metallurgy in modern Belarus. “The main research and the greatest volume of production output are concentrated under the auspices of the Minsk-Molodecheno Powder Metallurgy Association. Some 2055 tons of construction, tribo-technical and electrotechnical products were made and delivered in Belarus in 2007.” The industry is modernising. Technology for hot pressing of plasticised powder mixtures was adopted in 2007-2008 and modern technology for high-temperature sintering and hardening of parts from powder steels is in use. Sintering is developing a high-tech aspect in Belarus with the introduction of selective laser sintering of metal powders.
24
MPR April 2009
In manufacturing, pilot and industrial batches of PM “block rings” for the Belarus tractor gearbox have been delivered. Production technology has been optimised to minimise post-manufacture finishing and the first batch of integrated cone ring parts has been delivered. An industrial batch of parts for hand tools has also been delivered. Physical vapour deposition methodology in the copper-plating industry is planned for introduction in the near
100
future, replacing galvanic methods currently in use. Spreading the arc of powder technology, Belarus is developing ceramic injection moulding and has already seen some success. Pilot samples of parts of alumina-based pneumodrive distributor system for lorry brakes have been delivered and zirconia-based watch bodies have been made by ceramic injection moulding. The main PM trends in Belarus are:
100
300
755
100 179
200
Molodechno PM Plant
BATE
PM Institute
BelAZ
Ferrit Ent.
Ertex Ent.
All Figure 1. Powder production output in the Republic of Belarus from different plants in 2007.
0026-0657/09 ©2009 Elsevier Ltd. All rights reserved.
å 3DUWV IRU PRWRU DQG WUDFWRU DQG DJULculture machines- frictional disks and friction assembly linings; sliding bearings, gears and synchronisers; å (OHFWURWHFKQLFDO SDUWV IRU HOHFWULF machine collectors, electric brushes, electric contacts, hard and soft magnetic ferrites and ceramic isolators; å 3URGXFWLRQRISRURXVSURGXFWVIRUILOtration of liquids, gases, metal melts, heat exchangers, noise silencers and fire barriers; å 3URGXFWLRQ RI SRZGHUV IRU KDUG DQG soft magnetic soft ferrites, bronze and special powders for gas and thermal spraying; å *DVDQGWKHUPDODQGLRQDQGYDFXXP methods for applying wear and corrosion-resistant coatings as well as decorative coatings; å 'LDPRQGWRROSURGXFWLRQ The products of the 16 PM enterprises mentioned above powder metallurgy are varied, and used for both in-house assembly shop completion in bigger enterprises and for delivery to other consumers (Figure 1). Products of black and coloured metals powders, frictional compositions on steel bases and ferrite powder products are used more widely in the country. More than 700 tons of construction and anti-frictional products; about 1000 tons of ferrite powder products; more than 200 tons of electro-technical products( such as collectors for starters and electric brushes) and more than four tons of hard alloy products were manufactured in 2007. (Figure 2) Professor Ilyuschenko: “A number of technological processes protected by patents of Republic of Belarus and other countries have been developed and adopted under industrial conditions by Powder Metallurgy Institute specialists together with Production Republican Unitary Republican Production Enterprise of the Molodecheno Powder Metallurgy Plant to make parts from metal powders. Cold stamping of sintered parts made from black and coloured metal powders, the peculiarity of which are great plastic changes in sintered material form accompanied by its intensive packing and strengthening. “Car starter motor parts that are the equal of products manufactured by traditional metal working are made using to this technology. The method devel-
metal-powder.net
6 306
3 400
290 629
Ferrits
Structural parts and slide bearing
Frictional disks and klutchs
Electrotechnikal parts
Hard metal
Porous materials and heat pipe
Figure 2. Issue output for different types of powder production in the Republic of Belarus..
oped for sintering multi-component frictional material on steel bases is characterised by higher efficiency than traditional methods. The process is widely used in Production Republican Unitary Republican Production Enterprise’s PM plant in Molodecheno and State Powder Metallurgy Research Institute in making frictional disks.” The technology for solder – sintering of freely sprinkled frictional layers on steel base without galvanic copper coating introduced what is essentially a simplified technology for making frictional disks (Figure 3). As in the case of traditional soldering process, the connected surfaces are processed with a liquid solution of active flux to remove oxides from the base layer surface as well as for protection of connected surfaces from interaction with the environment, for reduced surface tension and increased spreading of liquid soldering agents. The composition developed -
“active water flux” – is a mixture of zinc chloride, ammonia chloride and copper chloride salts. Its interaction with iron leads to the formation of easily melted iron chloride. An active reducer for surface oxides is the nitrogen and hydrogen sintering furnace atmosphere. The solder – sintering process is carried out by passing the discs through belt furnaces. Subsequent operations are identical to the traditional technology The strength of items such as frictional disks for tractors, made by Belarusdeveloped technology, are certified by bending tests, as shown in Figure 3. As seen, the strength of the bimetal compound is high, a 180° bend does not result in separation of soldered metal ceramics and the steel base stripping. That is the main requirement for operational quality control of compound strength. Pilot data have shown that the strength of soldered compound-steel *IULFWLRQDOPDWHULDO0.FRQVWLWXWHV
Figure 3. Tractor frictional disk with two-sided soldered frictional layer after tests on compound strength.
April 2009 MPR
25
Figure 4. Experimental samples of cone ring parts for the synchroniser assemblies of tractor gearboxes.
5.41-5.6MPa which is by 10% better than the compound strength obtained by traditional method of applying freely sprinkled layer on coppered base. The replacement of the intermediate galvanic copper sub-layer by PM copper increased intermediate strength by 10-15%. This combination has proved to be cheaper and ecologically better since the galvanic copper plating process has come to an end. In a further development hard flux has been introduced into the frictional material, providing a further ecological boost and cost reduction. The method for producing heavily loaded sliding bearings with the use of infiltration of steel sintered bodies by
antifriction bronze melts is very promising. Such bearings are used in pivots of the front suspension bracket of dump trucks and lorries. Similar technology is also used in making bimetal bodies of blocks of axial and piston pumps and motors in which working surfaces are coated with anti-frictional powder layers. To carry out calculations and completion of technological processes for obtaining PM construction by hot pressing, the properties of diffused and alloyed powders of the following compoVLWLRQV 'LVWDOR\ $( & XVHG IRU making block rings of synchronisers for à%HODUXVá JHDUER[HV DQG 'LVWDOR\ '&
Figure 5. Experimental sample parts of a car braking system made by ceramic injection moulding of alumina-based ceramics.
26
MPR April 2009
0,3%C for making cone rings for synchroQLVHUVZHUHUHVWXGLHG'HQVPL[SRZGHU RQWKHEDVLVRI'LVWDOR\$(JUDSKLWHDQGSODVWLFLVHU'1KDVWKH following chemical composition: iron – base; molybdenum – 0.5%; nickel – 4%, copper – 15%, graphite –0.3% [5]. On the basis of literature data analysis and experimental investigation performance, the following main properties of materials under study were defined: fluidity of powders, sprinkled density, density- temperature and pressing pressure relationship curve, elastic after action, Poisson coefficient, Young’s modulus and fluidity limit. Taking into consideration the data obtained, we cal-
Figure 5a. Experimental samples of watch bodies obtained by CIM from zirconium ceramics.
metal-powder.net
a
b
c
Figure 6. Selective laser sintering installation developed in the Powder Metallurgy Institute.: a – general view; b –working chamber; c –technology platform
culated the optimal cycle for heat pressing stepped parts such as a ring with clamp and experiments on technology completion for obtaining block rings for a synchroniser of a “Belarus” tractor gearbox were carried out. Total density of block ring pressing pressed from 'LVWDOR\ $( SRZGHU E\ KHDW SUHVVLQJ method was 7.2 – 7.25g/ cm3. Shrinkage after sintering was 0.5%. It has been established that the blocking ring tooth after sintering has the greatest density in comparison with other elements. At
metal-powder.net
the same time, tooth density at the top, at 7.31g/cm3, is lower than the density at the base, 7.37g/cm3. The ring hub also has irregular density distribution. The influence of heat pressing, temperature and sintering time on material structure, properties and sizes of FRQH ULQJV PDGH IURP SRZGHU 'LVWDOR\ AE with additive 0.6%C has been studied. (Figure 4) If the synchroniser block rings are produced by thermal pressing methods by a number of companies, the attempt to get a constantly loaded cone
ring by this technology and in accordance with our data is a first. It has been established that sizes of pressing obtained by heat pressing increase by 0.1 – 0.2%. After sintering at 1170˚C in a nitrogen and hydrogen atmosphere they 0.4% – 0.5%. Parts sintered at 11700C for an hour have higher mechanical properties and satisfactory hardness (170 HB) for subsequent final plastic deformation. Annealing at 750 ˚C for two hours and slow cooling leads to reduced hardness of ring up to 140-160
April 2009 MPR
27
140-160 HB. Calibration for obtaining required sizes must be made after pressure annealing to 650 MPa. The problem for obtaining products of complex form, exact sizes and high density can be solved with the use of modern technology and equipment for injection forming of powder materials. The Powder Metallurgy Institute has acquired an installation for metal and ceramic injection moulding (MIM/CIM) for investigating processes of injection forming of complex form products of plasticised mixtures of metal or ceramic powders with part volumes up to 100 cm3, and maximum casting pressure up to 100 MPA. Additionally researchers are looking at other parameters such as granule bin heating up to temperatures of 150 – 200˚C; cast form locking effort of 250 – 310 MPA; productivity up to 20 cycles per hour (not less than 3 kg per hour). The first samples of parts – golden couple of pneumodrive system of car brakes (Figure 5) and watch body (Figure 5a) were obtained from plasticized ceramic mixtures Catamould. Multipurpose installation of powder laser stereolithography (selective laser sintering) has been developed and made by Powder Metallurgy Institute. It has a set of unique technology possibilities and great investigative potential [7] (Figure 6). The installation is designed for obtaining solid products of complex form made from metal and polymer powders. The system produces high precision components and the Institute has not spared expenditure on preparation or marketing of finished products. The equipment installed can operate as a laser sintering device or be used for laser melting. In the first case, surface melting of powder particles in layers and their combination by forming liquid metal contact necks is what allows in most cases porous the creation of products with given operational properties in preserving structure and phase composition of the initial material. In the second case, full powder melting in layer is used and products are obtained with virtually zero porosity. The installation is designed for sintering a wide range of materials, the melting temperature of which can differ. The total dimensions of soldering products do not exceed 50 ⫻ 200 ⫻ 200. Powders,
28
MPR April 2009
preferably spherical, with the size from 20µ to 400µ are used for sintering. Laser radiation is focused and directed perpendicular to the sintered layer plane. The selective laser sintering process occurs on vertically moving technology platform with the help of a linear step drive. The platform is located in working chamber with a protective atmosphere. The delivery of powder portions to the technology platform and formation of powder layers with given thickness is carried out with the help of a scale. Laser ray scanning in the horizontal plane at a given trajectory and sintering area observation with the help of video is made with the help of an optical system installed on two mutually perpendicularly connected linear step drives. Laser radiation is generated by an optic quant generator on the basis of a monocrystalline alumo-yttrium garnet alloyed by trivalent neodymium <$* 1G), working at a wavelength of 1064 nm (infrared radiation) with impulse repetition frequency up to 50 Hz. The preparation of the virtual model of product, software control for installation work, technology mode designation and their control in a real time regime is carried through by overall computer control. Professor Ilyuschenko says: “Powder metallurgy in Belarus is developing successfully. Advanced imported technologies are being adopted and are supporting and enhancing core knowledge already in the country. The opportunities provided by new technologies are being taken by researchers in the republic’s research institutes and the larger enterprises.The priority trend is the development of new sintered frictional materials, improved technology of production of frictional disks for tractor and road making vehicles. Our own investigations are carried out and new technologies for formation of powders according to selective laser sintering method are being developed.”
References 1. 40 years of powder metallurgy in the Republic of Belarus/ under editorVKLS RI ($ 'RURVKNHYLFK 9LW\D] 3 A, Zharin A E, Ilyushchenko A Ph et DO 0LQVN à.RYFKHJá S LQ Russian). 2. Modern sintered friction materiDOV 'PLWURYLFK $ $ ,O\XVKFKHQNR $
3.
4.
5.
6.
7.
3K 6\URH]KNR * 6 6KLSLWVD 1 $ Materials of reports of International Specialised scientific and engineering workshop,Minsk, April 15-16 2008. Minsk: Powder Metallurgy Institute, 2008, p.6-14 (in Russian) Frictional layer soldering to steel EDVH6\URH]KNR*63DVKFKXN6( *UL]HO39HWDO3RZGHUPHWDOOXUJ\ on motor and tractor machine building. Welding and cutting of materials .Materials, technologies and equipment for applying protective coating: International scientific and engineering symposiums, Minsk, March 28-30, 2007: materials of reports.Minsk: Powder Metallurgy Institute, 2007,p.34-38 ( in Russian). Tribotechnical properties of powder antifrictional materials used for friction assembly of axial and piston pumps/ '\DFKNRYD / 1 9RURQHWVND\D /
The authors This feature draws on Powder metallurgy of Belarus: science and production, a SDSHUE\$,O\XVFKHQNR96DYLFKDQG * 6\URHJNR ZKR DUH OHDGLQJ UHVHDUFKers in the Belarus industry. It was given at Euro PM 2008 in Mannhiem. 1. Powder Metallurgy Institute of NASc of Belarus, 41, Platonov Str., Minsk, 220005 Belarus 2. Molodechno Powder Metallurgy Plant,