Fluxes for Lead-Free Galvanizing U.S.Patenf 5437,738. Aug. 1, 1995
composition containing said water-dispersed, film-forming crosslinkable polymer system and dispersed water-swellable clay.
Y Gerenrot et al., Allison Park, Pa A preflux for galvanizing steel comprising S-30% zinc chloride, 2-20% ammonium chloride, O.l-1.0% boric acid or salt thereof. and O.l-2.0% inhibitor.
Polyurethane-Based Multicolor Paint U.S.Patenf 5,437,719. Aug. 1, 1995 J.E Lynch and J. Predkelis, assignors to Multicolor Specialties Inc., Cicero, 111. A method for making an aqueous multi-
color paint having a discontinuous aqueous phase dispersed in a continuous aqueous phase, one composition containing a waterdispersed, film-forming, crosslinkable polymer system selected from the group consisting of a polyurethane system, a carboxylated polymer system, and mixtures thereof, dissolved cellulose material selected from the group consisting of hydroxy (lower alkyl) cellulose, alkali metal carboxylated (lower alkyl) cellulose, and mixtures thereof, and pigment; the other
pearlite takes place thereby producing a patented brass-plated steel wire; and further cooling to ambient temperature.
Coated Abrasive U.S. Patent 5,437,754. Aug. 1, 1995 CD. Calhoun, assignor to 3M Co., St. Pau/, Minn.
Process for Patenting and Brass Plating Steel Wire U.S. Patent 5,437,748. Aug. 1, 1995 A. W. Bhagwaf and E.E Riggenbach,assignors to The Goodyear Tire & Rubber Co., Akron, Ohio
A process for simultaneously parenting and brass plating a steel wire, which comprises continuously passing the wire through a molten mixture of copper and zinc to apply a brass coating thereto, wherein the molten mixture is maintained at a temperature in the range of 930-about llOO”C, and wherein the steel wire has a residence time in the range of 6-15 set, which is sufficient for the steel to be austenitized; continuously wiping excess brass from the austenitized wire as it exits the molten mixture to attain a brass-coated steel wire having a coating weight in the range of 28 grams of brass per kilogram of the steel wire; cooling the wire to a quenching temperature in the range of 5OM5O”C until a transformation from austenite to
An abrasive article having precise lateral spacing between abrasive composite members.
Corrosion-Resistant Aluminum
Coating for
U.S. Patent 5,437,740. Aug. 1, 1995 J. W. Bibber, assignor to Sanchem Inc., Chicago
A method of protecting nonanodized aluminum or aluminum alloy with a nonchromium coating comprising contacting with an aqueous solution containing as the essential ingredients an alkali metal permanganate and an aluminum nitrate (at least 760 ppm of permanganate and O.lO10.0% of aluminum nitrate); maintaining the pH of the solution at 254.0, maintaining the temperature at 140_170”F, immersing for at least 20 seconds to form a protective conversion coating on the
GETFIXTURES CLEAN BETTER ANDEASIER!
Your Bayco oven will get your coating line fixtures dry and clean so easily, your entire operation will run smoother. And you’ll be getting rid of dangerous, expensive chemicals that create waste disposal problems for you. Bayco ovens are the best-engineered, most reliable, heaviest-duty cleaning ovens for the metal finisher. Ask for more information now.
AN
Circle 092 on
100
reader
information card
EPOXYLITE
COMPANY
Circle 012 on reader information card
METAL
FINISHING
??
APRIL 1996
composition containing said water-dispersed, film-forming crosslinkable polymer system and dispersed water-swellable clay.
Y Gerenrot et al., Allison Park, Pa A preflux for galvanizing steel comprising S-30% zinc chloride, 2-20% ammonium chloride, O.l-1.0% boric acid or salt thereof. and O.l-2.0% inhibitor.
Polyurethane-Based Multicolor Paint U.S.Patenf 5,437,719. Aug. 1, 1995 J.E Lynch and J. Predkelis, assignors to Multicolor Specialties Inc., Cicero, 111. A method for making an aqueous multi-
color paint having a discontinuous aqueous phase dispersed in a continuous aqueous phase, one composition containing a waterdispersed, film-forming, crosslinkable polymer system selected from the group consisting of a polyurethane system, a carboxylated polymer system, and mixtures thereof, dissolved cellulose material selected from the group consisting of hydroxy (lower alkyl) cellulose, alkali metal carboxylated (lower alkyl) cellulose, and mixtures thereof, and pigment; the other
pearlite takes place thereby producing a patented brass-plated steel wire; and further cooling to ambient temperature.
Coated Abrasive U.S. Patent 5,437,754. Aug. 1, 1995 CD. Calhoun, assignor to 3M Co., St. Pau/, Minn.
Process for Patenting and Brass Plating Steel Wire U.S. Patent 5,437,748. Aug. 1, 1995 A. W. Bhagwaf and E.E Riggenbach,assignors to The Goodyear Tire & Rubber Co., Akron, Ohio
A process for simultaneously parenting and brass plating a steel wire, which comprises continuously passing the wire through a molten mixture of copper and zinc to apply a brass coating thereto, wherein the molten mixture is maintained at a temperature in the range of 930-about llOO”C, and wherein the steel wire has a residence time in the range of 6-15 set, which is sufficient for the steel to be austenitized; continuously wiping excess brass from the austenitized wire as it exits the molten mixture to attain a brass-coated steel wire having a coating weight in the range of 28 grams of brass per kilogram of the steel wire; cooling the wire to a quenching temperature in the range of 5OM5O”C until a transformation from austenite to
An abrasive article having precise lateral spacing between abrasive composite members.
Corrosion-Resistant Aluminum
Coating for
U.S. Patent 5,437,740. Aug. 1, 1995 J. W. Bibber, assignor to Sanchem Inc., Chicago
A method of protecting nonanodized aluminum or aluminum alloy with a nonchromium coating comprising contacting with an aqueous solution containing as the essential ingredients an alkali metal permanganate and an aluminum nitrate (at least 760 ppm of permanganate and O.lO10.0% of aluminum nitrate); maintaining the pH of the solution at 254.0, maintaining the temperature at 140_170”F, immersing for at least 20 seconds to form a protective conversion coating on the
GETFIXTURES CLEAN BETTER ANDEASIER!
Your Bayco oven will get your coating line fixtures dry and clean so easily, your entire operation will run smoother. And you’ll be getting rid of dangerous, expensive chemicals that create waste disposal problems for you. Bayco ovens are the best-engineered, most reliable, heaviest-duty cleaning ovens for the metal finisher. Ask for more information now.
AN
Circle 092 on
100
reader
information card
EPOXYLITE
COMPANY
Circle 012 on reader information card
METAL
FINISHING
??
APRIL 1996