The effect of cold work on the sensitization of 304 stainless steel

418

3.

ERRATA

Vol.

THE EFFECT OF COLD WORK ON THE SENSITIZATION Scripta

Metallurgica,

13,

179

OF 304 STAINLESS

13, No.

5

STEEL

(1979)

C.L. Briant and A.M. Table I I I of this a r t i c l e should read as follows.

Ritter

TABLE I I I Comparison of Results for Modified Strauss Test for Samples Pulled to 344.7 MN/m2 and 551.5 MN/m~ Before Sensitization Sensitizing Temperature l Hour Sensitize 24 Hour Sensitize 344.7 MN/m2 551.5 MN/m2 344.7 MN/m2 551.5 MN/m2 (°c) 450°C No Attack Partial Attack* Partial Attack Partial Attack

500°C

Partial Attack

Partial Attack

Partial Attack

Failure*

650°C

Failure

Failure

Failure

Partial Attack

*Partial attack means that corrosion had occurred but the sample did not break upon bending. Failure means that the sample broke into two pieces upon bending. The information given in the original text is a l l correct including the description of this table. The only error was that the second temperature entered in this table should have been 500°C as given above and not 550°C as listed in the original table. All conclusions of the a r t i c l e are correct and remain unchanged. (Received March 19, 1979)